Halnn superhard launched new hard turning inserts BN-S20 for processing high hardness thermal spray welding parts

Halnn superhard launched new hard turning inserts BN-S20 for hard turning high hardness spray welding parts

Thermal spray welding typically include nickel-based alloys,iron-based alloys and cobalt-based alloy spray powder.According to different alloy spray coating layer spray welding hardness were applied to repair mechanical parts or to increase the metal surface properties; Spray coating thickness usually from 0.01mm to a few millimeters; Spraying coating/spray layer hardness ≥HRC50;Some spray welding layer hardness ≥HRC65;When the cutting tools of spray coating layer and spray welding layer always is to limit hard surface later period processing technology problems.

Compared with the sprayed coating,spray welding layer owns more significant advantage. However,due to the temperature up to 900 ℃ after matrix local heating in remelting processing,it will have a greater thermal deformation.

The Performance of Halnn BN-S20 cutting tool used for Machining spray welding layer:

1.BN-S20 CBN Cutting Tools is suitable for machining high hardness spray welding layer of the surface hardness HRC45-79,such as machining Ni60,Fe65 and tungsten carbide spray welding layers of surface hardness HRC65 .

2. BN-S20 grades superhard cutting tool is a CBN cutting tool material grades,Halnn superhard cutting tool independent research and development aiming at high hardness and processing properties of an alloy build-up welding layer and spray welding layer is a national key scientific and technological project results,utility model patents products.

3. Suitable for cutting processing spray coating and spray welding hard surface as following:A variety of hard surface cutting processing about flame spraying, powder coating oxyacetylene flame,oxyacetylene flame wire spray,oxyacetylene flame spray, HVOF,arc spraying,plasma spraying,atmospheric plasma spraying,cutting low pressure plasma spraying etc.

4. Suitable for cutting the following materials spray welding layer and sprayed layer: WC spray welding layer, nickel-based alloy spray welding layer, cobalt-based alloy build-up welding layer, Hastealloy spray welding layer, Ni60 spray welding layer,88WC12CO, 86WC10CO4Cr and carbonized chromium removal spray welding layer; and suitable for high hardness alloy steel roughing and finishing.BN-S20 grades cutting tool processing spray welding layer and build-up welding layer cutting parameters :

Processing Case A: 

BN-S20 grades cutting tool is a machine folder indexable inserts, also suitable for processing spray welding layer and spray layer hard surface: WC spray welding layer, nickel-based alloy spray welding layer, cobalt-based alloy build-up welding layer,

For example, processing cobalt-based alloy spray coating materials,Spray coating layer thickness: 2mm; Spray coating layer hardness:HRC60;Linear speed: V = 70--130m / min;Feed rate:0.7~

0.8mm/ r;Cutting Depth: ap=1.7mm;Cutting tool life: the life of each blade edge 150 minutes; 8 

cutting edge;

Processing Case B:

For example, processing hardness more than HRC65 of tungsten carbide spray welding layer, adopt the line speed :V = 85M / min; feed amount: ap = 0.65mm; BN-S20 processing efficiency and cutting tool life exhibited irreplaceable advantages.

Processing Case C: 

Machining nickel base alloy spray welding layer,adopting the line speed :Vc = 180m / min high-speed cutting; Use life is 6--10 times of ceramic inserts.

Hastelloy spray welding layer, Ni60 spray welding layer, 88WC12CO, 86WC10CO4Cr and carbonized chromium spray welding layer processing; BN-S20 cutting tool can process hardness over HRC65 spray welding layer and the spray layer,BN-S20 is a composite hard surface machining and superhard processing cutting tools special grades.

More information,http://www.halnntools.com/ ,Or contact with us halnntools@gmail.com ,skype:cbn_inserts_angels 

Halnn Bn-S20 CBN inserts used for hard turning Mill rolls Hard surface field

Halnn Bn-S20 CBN inserts used for hard turning Mill rolls Hard surface field

 

So-called hard surface process is collected surface build-up welding,spray welding,spraying,laser cladding technology,Surface heat treatment or nitriding process,etc.The surface of the work piece to obtain higher hardness, wear-resistance corrosion resistance,impact resistance, etc.Aiming at hard surface process,HALNN superhard developed a non-metal adhesive cubic boron nitride cutting tools BN-S20. Specific processing schemes are as follows. 1.Halnn superhard non-metallic adhesive CBN cutting tools BN-S20 rough turning surfacing rolls solution:     Processing Materials: Cobalt-based alloys；Processing parts: Surfacing Rolls(hardness HRC45-55);Cutting tools model: BN-S20；Processing procedure: External turning;Cutting parameters:ap=2.5mm，Fr=0.12mm/r,Vc=65m/min；Processing type: Wet cuttingProcessing effect: Compared to carbide cutting tools: The cutting speed of our cutting tools is 4.5 times higher than carbide cutting tools,cutting tool lifetime is 12 times of carbide cutting tools.  2.Halnn superhard non-metallic binder Hard Turning inserts BN-S20 rough machining Spray welding rolls solution: Processing parts: Spray welding parts；Processing materials: Nickel-based alloy powder spray welding parts;Hardness:HRC50Cutting tools model: BN-S20,Processing procedure: External turning,Wet cuttingCutting parameters: ap=1.5mm,Fr=0.15mm/r,Vc=145m/min；Processing effect: Compared Halnn BN-S20 model number with some European brand PCBN cutting tools:cutting speed in the same situation,HALNN BN-S20 cutting tool lifetime is 2 times of PCBN cutting tools life,and cutting tool flank is normal wear,rather than collapse damage,rupture. 3.Halnn superhard non-metallic binder CBN cutting tools BN-S20 rough machining spraying rolls solution: Processing Parts: Cobalt base spare parts, spraying thickness of 2 mm;Processing Materials: Cobalt-based alloy powder spraying roller;Hardness:HRC60Cutting tools model: BN-S20；Roughing cutting parameters: Vc=70m/min,Fr=0.7-0.8mm/r；ap=1.7mm；Finishing cutting parameters: Vc=120m/min,Fr=0.25mm/r;Processing effect: HALNN BN-S20 model number and carbide cutting tools compared: The cutting speed is carbide cutting tools 6 times,Cutting Depth is 3 times of carbide cutting tools,not only improved the processing efficiency,but also reduce processing costs. 4.Halnn superhard non-metallic adhesive CBN cutting tools BN-S20 finishing Laser cladding rolls solution:
Processing parts: Hydraulic prop；Processing Marterials: 27SiMn(The surface hardness after laser cladding is about HRC55);Processing procedure: Semi-finishing and finishing;Cutting tools model: BN-S20 CNMN120712;Cutting parameters: ap=1mm，Fr=0,15mm/r，Vc=145m/min；Processing type: Dry cuttingProcessing effect:Compared to carbide cutting tools: Not only improve processing efficiency,reduce production time,saving processing costs, and surface finish to Ra 0.4, long cutting tool life.

More information,Please check http://www.halnntools.com/jjfa/19.html ,Or E-mail to ushalnntools@gmail.com ,skype:cbn_inserts_angels

Heavy interrupt turning Gears used CBN inserts BN-S20

In current times,there are so many new type cutting tools appeared,and they said that their products can satisfy the customers requirements;like interrupt turning,hard turning and grinding.But actually when manufacturers used their CBN inserts,they will find it difficult to machining ,and it will be chipping easily.

Halnn always devoted to satisfy different requirements of the customers ,so Halnn researched new grade BN-S20 CBN inserts ,specially for interrupt turning Gears ,and when it used in the actual conditions,they can easily solve their problems,and they also make the video for us ,please check as follows:

And if you would like to know more details about interrupt turning Gears ,contact with us halnntools@gmail.com,whatsapp:+8618695866134,skype:cbn_inserts_angels 

The Application of turning steel iron rolls with Halnn superhard CBN inserts

The Application of turning steel iron rolls with Halnn superhard CBN inserts

Part 1 The grade options of common clamp machine cutting tools which is used for turning steel iron rolls

Machining large scale steel iron rolls usually use heavy rolls milling, the common clamp insert holder which is used for large scale steel iron roller is 40*40 mm;common inserts holder angle is 45°clamp turning inserts or Arc turning inserts.Some small scale steel iron rolls use 25*25 and 32*32 mm clamp turning inserts holder.The option of the clamp turning insert holder main angle depend on the roller“ length-diameter ratio”, The slender rolls usually use 90°or 75°angle clamp turning inserts,Turning “Sturdy roller”usually use 45°clamp turning inserts or Arc turning inserts.

Part 2 The options of CBN inserts size and grade depending on turning cutting allowance and processing situations

When turning cast iron rolls with BN-K1 grade CBN cutting tools,we usually use RNMN200800,RNUN200800,RNMN150700,RNUN160800,RNUN150716,RNMN150716 

grade CBN cutting tools .

When turning forged steel cold roll with BN-S20 grade CBN inserts,we usually use SNMN120712, SNMN120412,SNMN120408,RNMN120400 grade CBN cutting tools .

Clamp turning inserts and CBN inserts

Part 3 The options and the Cutting parameters guidance of CBN inserts which used for turning mill rolls

The option principle:

1.the mill rolls materials

2.The mill rolls hardness

3.The mill rolls cutting allowance and Heat-treatment method

Depending on the milling rolls materials which is corresponding with the cutting inserts grade used for turning steel iron rolls ,it can be divided into 3 sorts :

a.Turning the low-hardness rolls

Ductile Cast Iron rolls,High alloy cast iron rolls usually used for heat-rolls,support-rolls,intermediate-rolls,the feature is that hardness is lower comparing to working-rolls.It can turning common alloy cutting tools and the common cutting tools grade is YG 6 or YG 6X.

b.Turning high hardness cast iron rolls

When turning chilled cast iron rolls (include unlimited chilled cast iron rolls),High nickel chrome rolls,high chrome rolls,boron high speed steel rolls, semi-steel rolls (including casting semi-steel rolls and high-carbon steel semi-rolls);nickel-chromium-molybdenum centrifugal composite rolls,Rolls rough usually have Porosity, trachoma,sand bag defects because of the rolls high hardness.So the tools need well impact resistance, heat resistance and wear resistance. In the past ,this kind rolls usually use ceramic cutting tools,the cutting tools will easily chipping.

In current times,People usually use BN-K1 grade CBN inserts machining this kind rolls. BN-K1 grade CBN inserts not only insist the excellent property of high hardness and well impact resistance ,but also have well impact roughness ,can not easily chipping ,and can pull shortage roughing rolls. BN-K1 grade CBN inserts is the best impact resistance high hardness CBN inserts in the current times.This grade CBN inserts can obey large cutting depth,high metal cutting ratio,the common cutting parameters as follows :

For BN-K1 grade Halnn CBN inserts turning HSD82 hardness high nickel-chromium cast iron rolls：Unilateral cutting depth can arrive 12 mm;Feed rate is 1.5 mm/r.

The cutting parameters of turning high hardness cast iron rolls with Halnn BN-K1 grade CBN inserts

No.	Rolls Materials	Mill Rolls working layer hardness	Recommend Cutting Parameters
1	Casting High nickel-chromium	HSD72-82	Rough finishing	Vc=15-30m/min,ap=3-7mm,f=1-2.5mm/r
			Semi-finishing	Vc=20-40m/min,ap=4mm,f=1.5-2.5mm/r
2	Cast high chromium iron	HSD72-78	Rough finishing	Vc=10-20m/min,ap=3-7mm,f=0.5-1.2mm/r
			Semi-finishing	Vc=15-30m/min,ap=4mm,f=1.5-2.5mm/r
3	Cast High Speed Steel	HSD82-90	Vc=5-15m/min,ap=3-8mm,f=1-2.5mm/r
4	Casting Semi-steel	HSD55-65	Vc=30-60m/min,ap=4mm,f=1.5-2.5mm/r
5	High carbon Semi-steel	HSD65-72	Vc=25-50m/min,ap=4mm,f=1.5-2.5mm/r
6	Chilled cast iron	HSD50-70	Vc=25-50m/min,ap=4mm,f=1.5-2.5mm/r
7	Casting high-chromium steel	HSD68-75	Vc=20-45m/min,ap=4mm,f=1.5-2.5mm/r
8	Tungsten carbide roll ring	HRA88	Vc=10-15m/min,ap=1mm,f=0.3-0.7mm/r
9	Forging 9Cr2Mo	HSD92-105	Vc=10-25m/min,ap=4mm,f=0.5-1.2mm/r

c.Turning high hardness forged steel cold rolls:

For example,turning GCr15 Rolling bearing steel roll ,Cr3,Cr5 roller ;86CrMoV7,9Cr2Mo rolls.This kind roll rough is forge work piece, usually use as cold roll after heat-treatment ,the common inserts grade is BN-S20 grade CBN cutting inserts.

BN-S20 grade CBN insert is the research result of National key scientific project,it is made of non-metal adhesives and CBN refined powder ,and it not only follow BN-K1 grade inserts’ toughness ,but also especially researched for long iron material forged steel cold roll.When machining forged steel cold rolls,BN-S20 grade CBN cutting insert Wear-resistance will be about 3 times of common CBN cutting inserts .

The cutting parameters of BN-S20 CBN inserts turning forged steel cold roll

(1)For example ,turning Sweden cold working rolls (HRC67):cutting depth4-7mm,line speed 90m/min ,life time is 2.5 times than some foreign brand CBN cutting inserts .

(2)When turning repairing 9Cr2Mo cold working roll,it will have good effect with BN-S20 cutting insert,the cutting insert lifetime is 4 times than other domestic CBN cutting inserts. And when turning cold working rolls , Chapped parts not chipping can guarantee the safety use and economy of CBN cutting insert .

Part 4 Rolls materials and common questions

BN-K1 and BN-S20 grade CBN cutting insert Turning rolls hardness and materials Fluctuation range (Remark:when rolls hardness is less than HSD70,it can choose cemented carbide grade cutting inserts,such as YG6,YG6X ect .When rolls hardness is more than HSD75 or above HSD110,it can choose BN-K1 and BN-S20 grade cutting inserts (Choose cutting inserts grade according to the rolls materials )

Roll Materials and Roll hardness range Comparison chart

Remark: Halnn Superhard cutting tools research department remind you:when choose CBN inserts turning rolls,the rolls hardness is not the only  factor,the most important factor is rolls materials.

Halnn CBN Cutting inserts materials grade:

Grade	Type	Applications
BN-K10	Welded	Fit for continuous finish turning gray cast iron and wear-resistance cast iron material,such as finish turning brake drums, brake discs, flywheels, cylinder workpiece.
BN-K20		Fit for finish turning gray cast iron,powder metallurgy materials and high-speed finish turning boring
BN-H10		Fit for continuous finish turning and high-speed finish turning hardened steel materials ,like “turning instead of grinding” wheel gear and bearing .
BN-H20		Fit for medium/strong finish turning and high-speed finish turning harden materials,such as machining contoured shaft and high-precision gears, bearings and small bore
BN-S20	Solid	Perfect Impact resistance and wear-resistance,good choice for rough and semi-finish turning workpiece; widely used for machining gray cast iron ,wear-resistance cast iron  sand inclusion,white cast iron, and various  steel, hardened steel materials
BN-S30		Best wear-resistance and well impact resistance,fit for high-speed finish turning cast iron,and fit for high speed and efficiency boring, milling

Halnn CBN inserts application range:

1.High hardness cast iron/cast steel,like rough and finish turning high chromium cast iron,white cast iron,Ni-hard cast iron and Heat-resistant and wear resistant steel material,usually use for turning rolls,Impurities pump impeller and other high hardness wear part.

2.Turning high hardness work piece after heat-treatment ,such as hard turning hardened bearing steel,Carburizing steel,tool steel,mold steel after heat-treatment.

3.Other difficult cutting materials:Turning high temperature alloys, powder metallurgy ect.

4.High speed turning cast iron high-grade ductile iron,